SPECIFICATIONS DE CIMENT PORTLAND en 197 1 CEM II/A 42,5 R
US Standards BSS 12/1996 / British Standard DIN, EN 197
Euro Standard ASTM C 150 CEM II
CHEMICAL COMPOSITION MINIMUM MAXIMUM
Silicon Dioxide(Si02) 20.50 22.00
Aluminium Oxide (AI332O3) 4.60 5.30
Ferric Oxide Fe2O3 3.50 4.00
Calcium Oxide (CaO) 63.00 65.00
Magnesium Oxide Mg 0% 1.50 2.50
Sulphur Trioxide (SO3) 1.50 2.50
Loss of ignition (LOI ) 1.00 2.50
Insoluble residue % 0.10 0.70
Tricalcium silicate (C3S %) 50.00 54.40
Dicalcium silicate (C2S %) 14.20 18.20
Tricalcium aluminate (C3A %) 6.00 6.80
Tricalcium aluminio ferrice (C4AF%) 11.60
Chromium (Cr%) 2.00
COMPRESSIVE STHENGTH ISO/EN 197 1/2000 BS 4550 MORTAR
03 Days 2.65 34.2 Kg/cm2 / 07 Days 37.3 42.5 Kg/cm2
28 Days 52.8 54.6 Kg/cm2
PHYSICAL AND MECHANICAL PROPERTIES
Blain CM2/GR 2.900/3.200 Autoclave Expansion 0.05 / 0,16
Normal Consistency %27.5 Initial Setting Time (Hours ; Min)
1.20 1.60
Final Set Time(Hours : Mins) 1.70 3.10

ORIGINE : ESPAGNE
EMBALLAGE ET TRANSPORT MT / mois : Ciment emballé dans des sacs de 50 Kg
en Kraft triple épaisseur avec un film plastic à
l intérieur, avec une validité avec une validité de
plus de 6 mois et conditionné triple épaisseur avec
un film plastique à l intérieur, avec une validité de
plus de 6 mois et conditionné sur des palettes
contenant 30 sacs et protégés par film plastique.


Conditions tarifaires : selon quantité